用于与高压氢接触的成型品的聚酰胺树脂组合物及使用了其的成型品制造技术
2017-08-18 09:32:12 来源:齐鲁在线 编辑:K027_小凯乐Polyamide resin composition for molding articles in contact with high pressure hydrogen and molded article using the same
The invention provides a polyamide resin composition for molding contact with high-pressure hydrogen, the polyamide resin composition with polyamide resin (A) and ethylene / alpha olefin copolymer (B), the polyamide resin (A) containing six methylene amine from two units and the number of carbon atoms from 8 to aliphatic 12 of the two carboxylic acid unit, the ethylene / alpha olefin copolymer (B) with unsaturated carboxylic acid and / or its derivatives modified ethylene / alpha olefin copolymer (B). The invention provides a polyamide resin composition, the polyamide resin composition can get excellent softness and heat cycle resistance, even repeated high-pressure hydrogen filling, molding pressure unloading also inhibited the defects generated.
技术实现步骤摘要
【国外来华专利技术】
本专利技术涉及用于与高压氢接触的成型品的聚酰胺树脂组合物及将其成型而成的成型品。
技术介绍
近年来,为了应对石油燃料的枯竭、削减有害气体排放量的要求,将使氢与空气中的氧进行电化学反应而进行发电的燃料电池搭载在汽车上,将燃料电池发出的电供给至电动机而作为驱动力的燃料电池电动汽车受到关注。由于氢分子尺寸小,因而与分子尺寸较大的天然气等相比,容易透过树脂中;高压氢与常压的氢相比,在树脂中蓄积的量变多,等等,由于此等原因,对于此前的树脂制罐(tank)、管(hose)而言,存在以下问题:反复进行高压氢的充填及卸压时,发生变形、破坏。作为燃料电池电动汽车的用于存储氢气等的罐,例如,研究了具有金属制端部件、包围该端部件的聚酰胺树脂制的衬套及包围该衬套的含浸有热固性树脂的纤维的结构用层的罐(例如,参见专利文献1)。另外,作为气体阻隔性优异、即使在低温也具有优异的耐冲击性的氢罐衬套,例如,研究了将由包含聚酰胺6、共聚聚酰胺及耐冲击材料的聚酰胺树脂组合物形成的氢罐衬套用材料成型而成的氢罐衬套(例如,参见专利文献2)。另外,作为从加氢站向燃料电池汽车等充填氢气的管,研究了在内层中使用了尼龙、聚缩醛、乙烯-乙烯醇共聚物等的氢充填用管(例如,参见专利文献3)。现有技术文献专利文献专利文献1:日本特表2011-505523号公报专利文献2:日本特开2009-191871号公报专利文献3:日本特开2010-031993号公报
技术实现思路
专利技术所要解决的课题然而,对于专利文献1中记载的罐而言,由于反复进行高压氢的充填及卸压,导致反复承受-40℃以下~90℃以上的温度变化(热循环),...
技术保护点
一种用于与高压氢接触的成型品的聚酰胺树脂组合物,所述聚酰胺树脂组合物配合有聚酰胺树脂(A)和乙烯/α‑烯烃共聚物(B),所述聚酰胺树脂(A)包含来自六亚甲基二胺的单元和来自碳原子数8~12的脂肪族二羧酸的单元,所述乙烯/α‑烯烃共聚物(B